Hot Melt (For Apparel)

Series LSCHYS-G LSCHYS - W LSCHYS - E LSCHYS(三層)
Grade G091 G050 G070 G241 W012 W241 E615 E230 VE050 VE241
Basic Material Aliphatic Ester
Property Standard /Procedure Unit  
Softening Temperature SanFang Method *(1) 105±4 98±4 60±4 90±4 75±4 90±4 105±4 105±4 98±4 90±4
Elastic Recovery SanFang Method *(2) % NO NO NO 92% NO 92% 96% 92% NO NO
Melt Flow Index  ASTM D1238*(3) g/10min 10~15 8~14 4~10 10~20 20~30 10~20 50~60 2~10 20~30 10~20
Elongation ASTM D882 % 400-800 600~800 >1000 400~800 600~1000 400~800 800~1200 800~1200 600~1000 400~800
Tensile Strength ASTM D882  Kg/cm2 >350 >150 >250 >100 >35 >100 >150 >100 >200 >200
100% Modulus ASTM D882 Kg/cm2 20~30 20~30 20~30 20~30 2~8 20~30 5~15 10~20 30~40 30~40
Surface Pattern -  -  -  -  -  -  -  -  -  -
Surface Color  -  -  -  -  -  -  -    -  
Suggested Bonding Conditions Flat Heat Pressing
Heat Pressing Temperature 110 ~ 140
Pressure Kg/cm2 5 ~ 8
Press time sec 30 ~ 40
Washing Condition SanFang Method Up to 40 ℃
Applied Fabric *(4) Knit Woven Elastic Fabric Knit Woven
Carrier RP/PP/PET

 

These data are provided as general information only.
They are approximate values and not intended for use in preparing specifications.
Please contact us before writing specifications on this product.

※ LSCHYS-G,W,E Thickness (mm):0.05mm、0.07mm、0.10mm.
※ LSCHYS (Three Layer) Thickness (mm):0.10mm、0.15mm.
※ Standard Width (Inches):56";If the standard thickness or width of the specifications can be customized.

Remark
(1)     Softening Temperature: By Capillary Rheometer (Weight Load:5Kg, Rate:3 ℃/min)
(2)     Elastic Recovery: Please contact us, we’ll provide product instruction.
(3)     Melt Flow Index: g/10min  by 2.16kg ,175℃
(4)     Applied Fabric: Clients can provide the fabric for us to test.