Elastic hot melt (For Apparel)

San Fang is a elastic film manufacturer who has concentrated on continuous improvement in elastic film quality.

Series LSCHYS-E
Grade E615 E230
Basic Material Ester
Property Standard / Procedure Unit  
Softening Temperature SanFang Method *(1) 105±4 105±4
Elastic Recovery SanFang Method *(2) % 96% 92%
Melt Flow Index ASTM D1238 *(3) g/10min 50~60 2~10
Elongation ASTM D882  % 800~1200 800~1200
Tensile strength ASTM D882 Kg/cm2 >150 >100
100% Modulus ASTM D882 Kg/cm2 5~15 10~20
Suggested Bonding Conditions Flat Heat Pressing
Heat Pressing Temperature 150~170 120 ~ 150
Pressure Kg/cm2 5 ~ 8
Press time sec 30 ~ 40
Suggested Bonding Conditions Seam Sealing Machine
Glue Line Temperature 300~350
Roller Pressure Kg/cm2 3~6
Line Speed M/min 1~6
Washing Condition SanFang Method 25 to 60 ℃
Applied Fabric *(4) Elastic Fabric
Carrier RP

These data are provided as general information only.
They are approximate values and not intended for use in preparing specifications.
Please contact us before writing specifications on this product.

※LSCHYS-E Standard thickness (mm):0.05mm、0.07mm、0.10mm 
※ Standard Width (Inches):56";If the standard thickness or width of the specifications can be customized.

Remark:
(1)    Softening Temperature: By Capillary Rheometer (Weight Load:5Kg, Rate:3 ℃/min)
(2)    Elastic Recovery: Please contact us, we’ll provide product instruction.
(3)    Melt Flow Index: g/10min  by 2.16kg ,175℃
(4)    Applied Fabric: Clients can provide the fabric for us to test.

With more than 50 years of elastic film experience, San Fang is the best elastic film manufacturer supplying to all over the world.