Elastic hot melt (For Apparel)
San Fang is a elastic film manufacturer who has concentrated on continuous improvement in elastic film quality.
Series | LSCHYS-E | |||
Grade | E615 | E230 | ||
Basic Material | Ester | |||
Property | Standard / Procedure | Unit | ||
Softening Temperature | SanFang Method *(1) | ℃ | 105±4 | 105±4 |
Elastic Recovery | SanFang Method *(2) | % | 96% | 92% |
Melt Flow Index | ASTM D1238 *(3) | g/10min | 50~60 | 2~10 |
Elongation | ASTM D882 | % | 800~1200 | 800~1200 |
Tensile strength | ASTM D882 | Kg/cm2 | >150 | >100 |
100% Modulus | ASTM D882 | Kg/cm2 | 5~15 | 10~20 |
Suggested Bonding Conditions | Flat Heat Pressing | |||
Heat Pressing Temperature | ℃ | 150~170 | 120 ~ 150 | |
Pressure | Kg/cm2 | 5 ~ 8 | ||
Press time | sec | 30 ~ 40 | ||
Suggested Bonding Conditions | Seam Sealing Machine | |||
Glue Line Temperature | ℃ | 300~350 | ||
Roller Pressure | Kg/cm2 | 3~6 | ||
Line Speed | M/min | 1~6 | ||
Washing Condition | SanFang Method | ℃ | 25 to 60 ℃ | |
Applied Fabric *(4) | Elastic Fabric | |||
Carrier | RP |
These data are provided as general information only.
They are approximate values and not intended for use in preparing specifications.
Please contact us before writing specifications on this product.
※LSCHYS-E Standard thickness (mm):0.05mm、0.07mm、0.10mm
※ Standard Width (Inches):56";If the standard thickness or width of the specifications can be customized.
Remark:
(1) Softening Temperature: By Capillary Rheometer (Weight Load:5Kg, Rate:3 ℃/min)
(2) Elastic Recovery: Please contact us, we’ll provide product instruction.
(3) Melt Flow Index: g/10min by 2.16kg ,175℃
(4) Applied Fabric: Clients can provide the fabric for us to test.
With more than 50 years of elastic film experience, San Fang is the best elastic film manufacturer supplying to all over the world.